POLYPROPYLENE
TYPE COPOLYMER HOMOPOLYMER HOMOPOLYMER
RANDOM
MET KG FLOW(230 oC-2.12) 12.50 9.50 12.50
TENSILE YIELD STRENGT (50 mm/min) 3900.00 4800.00 5000.00
TENSILE YIELD ELONGATION (50 mm/min) 13.50 10.50 10.00
FLEXURAL MODULUS 1% SECANT (1.3 mm/min) 130000.00 200000.00 210000.00
NOTCHED IZOD IMPACT STRENGTH (73 oF/ 23 oC) 0.90 0.60 0.60
GARDNER IMPACT STRENGTH (73 oF/ 23 oC) 200.00 N/A N/A
HARDNESS,ROCKWELL 85.00 100.00 100.00
GARDNER IMPACT STRENGTH (- 22 oF/ -30 oC) N/A N/A N/A
MET KG FLOW(230 oC-2.12)
TENSILE YIELD STRENGTH (50 mm/min)
TENSILE YIELD ELONGATION (50 mm/min)
FLEXURAL MODULUS 1% SECANT (1.3 mm/min)
NOTCHED IZOD IMPACT STRENGTH (73 oF/ 23 oC)
GARDNER IMPACT STRENGTH (73 oF/ 23 oC)
HARDNESS,ROCKWELL
GARDNER IMPACT STRENGTH (- 22 oF/ -30 oC)

Answer 1

聚丙烯 键入共聚物均聚物均聚物 任意 遇见的KG流动(230 oc2.12) 12.50 9.50 12.50 拉伸出产量STRENGT (50 mm/min) 3900.00 4800.00 5000.00拉伸出产量伸长(50 mm/min) 13.50 10.50 10.00弯曲模数1%正割(1.3 mm/min) 130000.00 200000.00 210000.00刻凹痕了IZOD冲击强度(73 23 oC) 0.90 0.60 0.60 GARDNER冲击强度(73 23 oC) 200.00 N/A N/A坚硬,罗克韦尔85.00 100.00 100.00 GARDNER冲击强度(- 22 -30 oC) N/A N/A N/A问题补充：遇见的KG流动(230 oc2.12) 拉伸出产量STRENGT (50 mm/min) 拉伸出产量伸长(50 mm/min) 弯曲模数1%正割(1.3 mm/min) 被刻凹痕的IZOD冲击强度(73 23 oC) GARDNER冲击强度(73 23 oC) 坚硬,罗克韦尔 GARDNER冲击强度(- 22 -30 oC)